Size‐Induced Ferroelectricity in Antiferroelectric Oxide Membranes

Ruijuan Xu (1, 2) , Kevin J Crust (3, 2) , Varun Harbola (2, 3) , Rémi Arras (4) , Kinnary Y Patel (5) , Sergey Prosandeev (5) , Hui Cao (6) , Yu‐tsun Shao (7) , Piush Behera (8) , Lucas Caretta (9, 8) , Woo Jin Kim (2, 1) , Aarushi Khandelwal (2) , Megha Acharya (10) , Melody M Wang (11) , Yin Liu (12) , Edward S Barnard (13) , Archana Raja (13) , Lane W Martin (10) , X. Wendy Gu (14) , Hua Zhou (15) , Ramamoorthy Ramesh (16) , David A Muller (7) , Laurent Bellaiche (5) , Harold Y Hwang (2)

1 Department of Applied Physics
2 Stanford Institute for Materials and Energy Sciences
3 Department of Physics
4 CEMES-MEM - Matériaux et dispositifs pour l'Electronique et le Magnétisme
5 Department of Physics and Institute for Nanoscience and Engineering, University of Arkansas
6 Materials Science Division
7 Department of Applied and Engineering Physics
8 Department of Materials Science and Engineering
9 Brown Engineering - School of Engineering
10 Materials Sciences Division
11 Department of Materials Science and Engineering
12 Department of Materials Science and Engineering
13 The Molecular Foundry
14 Department of Mechanical Engineering
15 X-ray Science Division
16 Department of Materials Science and Nanoengineering

Despite extensive studies on size effects in ferroelectrics, how structures and properties evolve in antiferroelectrics with reduced dimensions still remains elusive. Given the enormous potential of utilizing antiferroelectrics for high‐energy‐density storage applications, understanding their size effects will provide key information for optimizing device performances at small scales. Here, the fundamental intrinsic size dependence of antiferroelectricity in lead‐free NaNbO3 membranes is investigated. Via a wide range of experimental and theoretical approaches, an intriguing antiferroelectric‐to‐ferroelectric transition upon reducing membrane thickness is probed. This size effect leads to a ferroelectric single‐phase below 40 nm, as well as a mixed‐phase state with ferroelectric and antiferroelectric orders coexisting above this critical thickness. Furthermore, it is shown that the antiferroelectric and ferroelectric orders are electrically switchable. First‐principle calculations further reveal that the observed transition is driven by the structural distortion arising from the membrane surface. This work provides direct experimental evidence for intrinsic size‐driven scaling in antiferroelectrics and demonstrates enormous potential of utilizing size effects to drive emergent properties in environmentally benign lead‐free oxides with the membrane platform.

Domains: Physics [physics]

Ruijuan Xu, Kevin J Crust, Varun Harbola, Rémi Arras, Kinnary Y Patel, et al.. Size‐Induced Ferroelectricity in Antiferroelectric Oxide Membranes. Advanced Materials, 2023, 35 (17), pp.2210562. ⟨10.1002/adma.202210562⟩. ⟨hal-04237736⟩